High Temperature Low Cycle Fatigue Data for Three High Strength Nickel-Base Superalloys
Report Number: AFWAL TR 80-4077
Author(s): Conway, J. B., Stentz, R. H.
Corporate Author(s): Mar-Test Inc.
Laboratory: Materials Laboratory
Date of Publication: 1980-06
Pages: 120
Contract: F33615-76-C-5245
DoD Project: 2304
DoD Task: 2307P1
Identifier: ADA097430
Abstract:
This report presents a summary of the high temperature low cycle fatigue data for three high strength nickel-base superalloys, Rene 95, AF-115, and AF2-1DA. The majority of tests were performed in strain control at 1200 F and 1400 F, and at frequencies of 20 cpm, 0.2 cpm, and 0.05 cpm. Conventional triangular waveform was used for most of the testing although strain dwell tests and some SLOW-FAST and FAST-SLOW tests were also included.
Provenance: IIT
Author(s): Conway, J. B., Stentz, R. H.
Corporate Author(s): Mar-Test Inc.
Laboratory: Materials Laboratory
Date of Publication: 1980-06
Pages: 120
Contract: F33615-76-C-5245
DoD Project: 2304
DoD Task: 2307P1
Identifier: ADA097430
Abstract:
This report presents a summary of the high temperature low cycle fatigue data for three high strength nickel-base superalloys, Rene 95, AF-115, and AF2-1DA. The majority of tests were performed in strain control at 1200 F and 1400 F, and at frequencies of 20 cpm, 0.2 cpm, and 0.05 cpm. Conventional triangular waveform was used for most of the testing although strain dwell tests and some SLOW-FAST and FAST-SLOW tests were also included.